Concretos
Nuestras referencias
Tenemos un panel muy amplio de productos. Así encontramos una solución para contestar a su demanda y adaptarse a cada tipo de hornos.
CONCRETOS DENSOS:
|
TEMP °C DE MAX. DE SERVICIO
| COMPRESION EN PLANO SECO A 105 °C kg/cm2
| MODULO DE RUPTURA SECO A 105 °c kg/cm2
| CANTIDAD NECESARIA kg/m3 COLADO
| VIDA EN ALMACEN (meses)**
|
| ALTA CALIDAD
|
| HR 22
| 1290
| 421.0
| 70.0
| 2040
| 12
|
| HR 25
| 1400
| 337.0
| 70.0
| 2040
| 12
|
| HW BAFLE MIX
| 1510
| 140.0
| 56.0
| 2080
| 12
|
| CALIDAD SUPERIOR
|
| AW ES CASTABLE
| 1400
| 224.0
| 56.0
| 1860
| 12
|
| HW ES CASTABLE
| 1425
| 316.0
| 70.0
| 1980
| 12
|
| UBC 45 ADTECH
| 1650
| 527.0
| 126.0
| 2320
| 6
|
| ALTA ALUMINA
|
| HARCAST
| 1540
| 352.0
| 70.0
| 2100
| 12
|
| REFCAST 60
| 1512
| 281.0
| 70.0
| 2215
| 12
|
| UCAST 60
| 1650
| 253.0
| 63.0
| 2220
| 12
|
| ALMEX DUR
| 1450
| 478.0
| 87.0
| 2400
| 12
|
| UBC 70 ADTECH
| 1705
| 703.0
| 106.0
| 2645
| 6
|
| UCAST 80
| 1870
| 330.0
| 77.0
| 2570
| 12
|
| AUTOFLUIDOS
|
| AUTOCAST 13 ADTECH
| 1315
| 490.0
| 70.0
| 1540
| 6
|
| AUTOCAST 14 ADTECH
| 1350
| 702.0
| 126.0
| 2050
| 6
|
| AUTOCAST 15 ADTECH
| 1480
| 840.0
| 70.0
| 2050
| 6
|
| AUTOCAST 16 ADTECH
| 1650
| 773.0
| 126.0
| 2480
| 6
|
| AUTOCAST 17 ADTECH
| 1650
| 703.0
| 168.0
| 2360
| 6
|
| EXTRA ALTA ALUMINA
|
| ULTRX 85 ADTECH
| 1732
| 406.0
| 86.0
| 2760
| 6
|
| CASTOLAST G/ADTECH
| 1870
| 619.0
| 127.0
| 2880
| 12
|
| ELECTROCAST 94/ADTECH
| 1870
| 344.0
| 112.0
| 2885
| 12
|
| CASTOLAST 97/ADTECH
| 1870
| 155.0
| 63.0
| 2630
| 12
|
| UBC 90 ADTECH
| 1870
| 443.0
| 155.0
| 3050
| 6
|
**=BAJO TECHO EN UN LUGAR FRESCO Y SECO
COMPOSICION QUIMICA
|
ALUMINIA PROMEDIO %
| SILICE PROMEDIO %
|
| ALTA CALIDAD
|
| HR 22
| 36.9
| 47.9
|
| HR 25
| 50.6
| 35.8
|
| HW BAFLE MIX
| 49.3
| 37.1
|
| CALIDAD SUPERIOR
|
| AW ES CASTABLE
| 43.0
| 42.0
|
| HW ES CASTABLE
| 50.0
| 35.0
|
| UBC 45 ADTECH
| 44.0
| 49.5
|
| ALTA ALUMINA
|
| HARCAST
| 54.0
| 34.0
|
| REFCAST 60
| 58.0
| 29.0
|
| UCAST 60
| 62.0
| 29.0
|
| ALMEX DUR
| 61.0
| 29.0
|
| UBC 70 ADTECH
| 73.0
| 22.7
|
| UCAST 80
| 82.0
| 10.0
|
| AUTOFLUIDOS
|
| AUTOCAST 13 ADTECH
| 46.0
| 43.0
|
| AUTOCAST 14 ADTECH
| 49.0
| 44.0
|
| AUTOCAST 15 ADTECH
| 46.0
| 45.0
|
| AUTOCAST 16 ADTECH
| 65.0
| 27.4
|
| AUTOCAST 17 ADTECH
| 70.0
| 25.5
|
| EXTRA ALTA ALUMINA
|
| ULTRX 85 ADTECH
| 86.3
| 8.5
|
| CASTOLAST G/ADTECH
| 93.5
| 0.5
|
| ELECTROCAST 94/ADTECH
| 92.0
| 0.8
|
| CASTOLAST 97/ADTECH
| 96.0
| 0.1
|
| UBC 90 ADTECH
| 95.0
| 3.3
|
CONCRETOS CONVENCIONALES
Los concretos convencionales son la combinación de granos refractarios con sistemas de liga hidráulica, que después de ser mezclados con proporciones definidas de agua, se pueden vaciar en el lugar para formar una pieza o estructura la cual se vuelve rígida por acción química.
|
TEMP DE MAX. OPERACION
| DENSIDAD kg/m3
| MOR kg/cm2
| CCS kg/cm2
| CLP %
|
|
|
|
110 °C
| 816.0 °C
| 1370 °C
| 110 °C
| 816 °C
| 1350 °C
| 110 °C
| 816 °C
| 1350 °C
|
| BASE ARCILLA
|
| CINACAST 40
| 1320
| 2.020
| 68
| 30
| 24
| 282
| 155
| -
| -
| -0.1
| -125
|
| CINACAST 48
| 1590
| 2.080
| 74
| 49.2
| 66
| 150
| 110
| -
| -
| -0.2
| 0
|
| ALTA ALUMINA
|
| CINACAST 60
| 1650
| 2.160
| 47
| 34
| 122
| 168
| 158
| 263
| -
| -0.2
| 1
|
| CINACAST ES
| 1371
| 2.200
| 100
| 60
| 150
| -
| -
| -
| -
| -
| -0.03
|
| CINACAST 80
| 1700
| 2.550
| 40
| -
| 85
| 360
| -
| 400
| -
| -
| -0.3
|
| CINAX AL 66
| 1815
| 2.723
| 100
| 80
| 200
| 230
| 160
| 300
| -
| -0.1
| -0.2
|
| CINAX AL 66-A
| 1815
| 2.804
| 110
| 75
| 200
| 747
| 420
| 750
| -
| -0.1
| -0.3
|
| CINAX AL 94
| 1815
| 2.700
| 70
| 50
| 120
| 320
| 280
| 800
| -
| -0.2
| -0.3
|
COMPOSICION QUIMICA
|
H2O %
| POROSIDAD %
| Al203 %
| SiO2 %
| ALCALIS + CaO %
| Fe203
| Otros %
|
| BASE ARCILLA
|
| CINACAST 40
| 10-13
| 25
| 39.7
| 36.9
| 13.3
| 7.7
| BAL
|
| CINACAST 48
| 10-12
| 25
| 48.5
| 43.2
| 6.0
| 0.9
| BAL
|
| ALTA ALUMINA
|
| CINACAST 60
| 10-12
| 16
| 57.8
| 35.6
| 2.9
| 7.0
| BAL
|
| CINACAST ES
| 11-12
| -
| 65.6
| 1
| 6.7
| 1.0
| BAL
|
| CINACAST 80
| 10-12
| 25
| 82.0
| 5.1
| 6.0
| 1.5
| BAL
|
| CINAX AL 66
| 8.0-9.0
| 16
| 96.0
| 0.1
| 3.0
| 0.1
| BAL
|
| CINAX AL 66-A
| 7.0-8.5
| 15
| 91.9
| 1.9
| 4.2
| 0.6
| BAL
|
| CINAX AL 94
| 8.0-10
| 16
| 94.0
| 1.9
| 4.0
| 0.6
| BAL
|
CONCRETOS AISLANTES:
|
TEMP MAX DE OPERACION
| DENSIDAD kg/m3
| MOR kg/cm2
| CCS kg/cm2
| CLP %
|
|
|
|
110 °C
| 816.0 °C
| 1370 °C
| 110 °C
| 816 °C
| 1350 °C
| 110 °C
| 816 °C
| 1350 °C
|
| LITE WATE 58 LI
| 1175
| 918
| 15
| 10.1
| 20
| 69
| 49
| 40
| -
| -0.3
| -
|
| LITE WATE 70
| 1260
| 1.250
| 24.6
| 14
| -
| 112
| 42
| -
| -
| -0.4
| -
|
| LITE WATE 80
| 1370
| 1.330
| 27
| 25
| 27
| 84
| 70
| 50
| -
| -0.1
| -0.7
|
| LITE WATE 80 ES
| 1370
| 1.315
| 27
| 61
| -
| 67
| 61
| -
| -
| -0.1
| -0.7
|
| CINAX AL BI 57
| 1815
| 1.202
| 23
| 17
| 23
| 35
| 23
| 70
| -
| -0.1
| -0.2
|
| LINS 50
| 1250
| 800
| 64
| -
| -
| -
| -
| -
| -
| -
| -
|
COMPOSICION QUIMICA
|
H2O %
| POROSIDAD %
| Al2O3 %
| SiO2
| ALCALIS + CaO %
| Fe2O3 %
| Otros %
|
| LITE WATE 58 LI
| 34.0
| 48.0
| 48.0
| 33.7
| 14.3
| 1.0
| BAL
|
| LITE WATE 70
| 31.2
| -
| 33.6
| 41.6
| 12.4
| 7.2
| BAL
|
| LITE WATE 80
| 32.5
| -
| 43.8
| 39.1
| 11.9
| 2.4
| BAL
|
| LITE WATE 80 ES
| 34.7
| -
| 46.7
| 36.0
| 12.1
| 2.0
| BAL
|
| CINAX-AL BI 57
| 18-21
| -
| 93.50
| 0.60
| 5.40
| 0.20
| BAL
|
| LINS 50
| 35.7
| -
| 69.4
| 19.0
| 8.4
| 0.5
| BAL
|
OTROS CONCRETOS AISLANTES
|
TEMP °C MAX DE SERVICIO
| COMPRESION EN PLANO SECO A 105 °C kg/cm2
| MODULO DE RUPTURA SECO A 105 °C kg/cm2
| CANTIDAD NECESARIA kg/m3 COLADO
| VIDA EN ALMACEN (meses)**
|
| HW LIGHT WEIGHT 16
| 870
| 6.0
| 3.0
| 400
| 12
|
| MICACRETE 7
| 980
| 25.0
| 14.0
| 720
| 12
|
| RM 50 BCF
| 1260
| 21.0
| 7.0
| 835
| 12
|
| RM 22 LW
| 1205
| 28.0
| 11.0
| 800
| 12
|
| CONCRETO ALMEX 55
| 1260
| 35.0
| 11.0
| 888
| 12
|
| HW LIGHT WEIGHT 25
| 1370
| 63.0
| 20.0
| 1300
| 12
|
| HW LIGHT WEIGHT 30
| 1650
| 84.0
| 29.0
| 1440
| 12
|
| RM 33 LW
| 1815
| 14.0
| 28.0
| 1360
| 6
|
COMPOSICION QUIMICA
|
ALUMINIA PROMEDIO %
| SILICE PROMEDIO %
|
| HW LIGHT WEIGHT 16
| 9.3
| 30.8
|
| MICACRETE 7
| 18.0
| 46.5
|
| RM 50 BCF
| 37.5
| 48.0
|
| RM 22 LW
| 41.0
| 40.0
|
| CONCRETO ALMEX 55
| 41.0
| 36.0
|
| HW LIGHT WEIGHT 25
| 43.0
| 35.2
|
| HW LIGHT WEIGHT 30
| 63.5
| 28.0
|
| RM 33 LW
| 92.0
| 0.1
|
CONCRETOS ESPECIALES
|
TEMP MAX DE OPERACION
| DENSIDAD kg/m3
| MOR kg/cm2
| CCS kg/cm2
| CLP %
|
|
|
|
110 °C
| 816.0 °C
| 1370 °C
| 110 °C
| 816 °C
| 1350 °C
| 110 °C
| 816 °C
| 1350 °C
|
| REF SIC 11 LI
| 1482
| 2.323
| 40
| 70
| 110
| 80
| 140
| 220
| -
| -0.2
| -0.3
|
| CINACAST AB
| 1290
| 2.160
| 116
| 91
| 162
| 590
| 440
| 540
| -
| -0.2
| -2.0
|
| CINACAST Zr
| 1320
| 2.720
| 130
| 112
| 160
| 830
| 870
| -
| -
| -
|
COMPOSICION QUIMICA
|
H2O %
| POROSIDAD %
| Al2O3 %
| SiO2
| ALCALIS + CaO %
| Fe2O3 %
| Otros %
|
| REF-SIC 11 LI
| 9.0-11
| -
| 12.0
| 1.5
| 2.9
| 0.5
| 82.5 (SiC)
|
| CINACAST AB
| 10-12
| 18
| 56.9
| 34.5
| 6.5
| 0.6
| BAL
|
| CINACAST Zr
| 9-10
| 17
| 62.0
| 7.2
| 6.3
| 0.5
| 23.2 (Zr02)
|
BAJO Y ULTRABAJO CEMENTO
Los concretos de bajo y ultrabajo cemento como su nombre lo indica contienen poco cementente y requieren de poca agua en su mezclado debido a la acción de agentes químicos especiales y a la distribución granulométrica, lo que proporciona alta resistencia a la abrasión y baja porosidad. Estos concretos requieren de vibración para su instalación.
|
TEMP MAX DE OPERACION
| DENSIDAD kg/m3
| MOR kg/cm2
| CCS kg/cm2
| CLP %
|
|
|
|
110 °C
| 816 °C
| 1370 °C
| 110 °C
| 816 °C
| 1350 °C
| 110 °C
| 816 °C
| 1350.0 °C
|
| CINALOW 50
| 1538
| 2.450
| 111
| 143
| 179
| 484
| 725
| 742
| -
| 0.00
| -0.2
|
| CINALOW 60
| 1650
| 2.540
| 143
| 187
| 291
| 638
| 682
| 809
| -
| -0.1
| -0.23
|
| CINALOW 70
| 1760
| 2.620
| 136
| 183
| 256
| 449
| 485
| 700
| -
| -0.2
| -0.08
|
| CINALOW 92 C
| 1870
| 3.200
| 72.3
| 55
| 115
| 440
| 310
| 700
| -
| 0.01
| -0.07
|
| CINALOW 98
| 1760
| 3.200
| 128
| 108
| -
| 373
| 530
| 630
| -
| 0.00
| -0.1
|
| CINAULTRA 60 XL
| 1650
| 2.620
| 52
| 96
| 254
| 236
| 397
| 1100
| -
| 0.04
| 0.21
|
| CINAULTRA 70 XL
| 1750
| 2.700
| 63
| 91
| 302
| 295
| 323
| 843
| -
| -0.3
| -0.02
|
| CINAULTRA 80 XL
| 1760
| 2.850
| 100
| 85
| 200
| 750
| 642
| 1000
| -
| 0
| -0.02
|
| NCM S25
| 1750
| 2.85
| 30
| -
| 30
| 170
| -
| 200
| -
| -
| -0.15
|
COMPOSICION QUIMICA
|
H2O %
| POROSIDAD %
| Al2O3 %
| SiO2
| ALCALIS + CaO %
| Fe2O3 %
| Otros %
|
| CINALOW 50
| 5.0-5.8
| 16.3
| 51.0
| 44.0
| 1.9
| 0.8
| BAL
|
| CINALOW 60
| 4.8-6.0
| 16.1
| 59.5
| 35.4
| 1.7
| 1.1
| BAL
|
| CINALOW 70
| 4.8-6.0
| 16.7
| 70.0
| 24.6
| 1.7
| 1.2
| BAL
|
| CINALOW 92 C
| 4.5-5.5
| 18.3
| 92.4
| 0.07
| 1.7
| -
| 5.0 (Cr203)
|
| CINALOW 98
| 4.2-5.2
| 18.0
| 97.8
| Tr
| 1.7
| Tr
| BAL
|
| CINAULTRA 60 XL
| 4.0-5.0
| 16.7
| 61.3
| 35.0
| 0.6
| 1.0
| BAL
|
| CINAULTRA 70 XL
| 4.0-5.0
| 18.0
| 68.3
| 27.0
| 0.7
| 1.2
| BAL
|
| CINAULTRA 80 XL
| 4.0-5.0
| 15.0
| 80.3
| 14.5
| 0.6
| 1.6
| BAL
|
| NCM S25
| 4.5-5.8
| 20.0
| 70.0
| 3.5
| 0.4
| 0.1
| 20.3 (SiC)
|
Go back to main menu
e-mail: armandojguerra@rirsaglass.com.mx
© Derechos reservados RIRSA GLASS. Actualizado en Febrero de 2002